Extremely high viscosity grease with solid lubricants
SKF LGEV 2 is a mineral oil based grease, using a lithium-calcium soap. Its high content of molybdenum disulphide and graphite, in conjunction with an extremely high viscosity oil, provide outstanding protection under the harshest conditions involving high loads, slow rotations and severe vibrations.
Extremely suitable for lubricating large sized spherical roller bearings subject to high loads and slow rotations, a situation where microslip is likely to occur
Extremely mechanically stable providing good water resistance and corrosion protection
Typical applications:
Trunnion bearings on rotating drums
Support and thrust rollers on rotary kilns and dryers
Bucket wheel excavators
Slewing ring bearings
High pressure roller mills
Crushers
| Available pack sizes | |
| Packsize | Designation |
| 35 g tube | LGEV 2/0.035 |
| 420 ml cartridge | LGEV 2/0.4 |
| 5 kg can | LGEV 2/5 |
| 18 kg pail | LGEV 2/18 |
| 50 kg drum | LGEV 2/50 |
| 180 kg drum | LGEV 2/180 |
| Electro-mechanical lubricant dispensers | |
| TLMR 101 series 380 ml refill (incl. battery) | LGEV2/MR 380B |
| TLMR 201 series 380 ml refill | LGEV 2/MR380 |
| Technical data | ||
| Designation | LGEV 2/(pack size) | |
| DIN 51825 code | KPF2K-10 | |
| NLGI consistency class | 2 | |
| Thickener | Lithium/calcium | |
| Colour | Black | |
| Base oil type | Mineral | |
| Operating temperature range | –10 to +120 °C (15 to 250 °F) |
|
| Dropping point DIN ISO 2176 | >180 °C (>355 °F) | |
| Base oil viscosity | ||
| 40 °C, mm²/s 100 °C, mm²/s |
1 020 58 |
|
| Penetration DIN ISO 2137 | ||
| 60 strokes, 10–1 mm 100 000 strokes, 10–1 mm |
265–295 325 max. |
|
| Mechanical stability | ||
| Roll stability, 72 hrs at 100 °C, 10–1 mm V2F test |
+50 max. ‘M’ |
|
| Corrosion protection | ||
| Emcor: |
– standard ISO 11007 – water washout test – salt water test (100% seawater) |
0–0 0–0* 0–0* |
| Water resistance | ||
| DIN 51 807/1, 3 hrs at 90 °C | 1 max. | |
| Oil separation | ||
| DIN 51 817, 7 days at 40 °C, static, % | 1–5 | |
| Copper corrosion | ||
| DIN 51 811 |
1 max 100 °C (210 °F) | |
| EP performance | ||
| Wear scar DIN 51350/5, 1 400 N, mm 4–ball test, welding load DIN 51350/4, N |
1,2 max. 3 000 min. |
|
| * Typical value | ||